Toyama, Takeshi*; Tanno, Takashi; Yano, Yasuhide; Inoue, Koji*; Nagai, Yasuyoshi*; Otsuka, Satoshi; Miyazawa, Takeshi; Mitsuhara, Masatoshi*; Nakashima, Hideharu*; Onuma, Masato*; et al.
Journal of Nuclear Materials, 599, p.155252_1 - 155252_14, 2024/10
Times Cited Count：1 Percentile：33.61(Materials Science, Multidisciplinary)We investigated the stability of oxide nano particles in oxide dispersion-strengthened (ODS) steel, which is a promising candidate material for next-generation reactors, under neutron irradiation at high temperature to high doses. MA957, a 14Cr-ODS steel, was irradiated with Joyo in Japan Atomic Energy Agency under irradiation conditions of 130 dpa at 502
C, 154 dpa at 589C, and 158 dpa at 709C. Three-dimensional atom probe (3D-AP) and transmission electron microscope (TEM) observation were performed to characterize the oxide particles in the ODS steels. A high number density of Y-Ti-O particle was observed in the unirradiated and irradiated samples. Almost no change in the morphology of the oxide particles, i.e. average diameter, number density, and chemical composition, has been observed in the samples irradiated to 130 dpa at 502C and to 154 dpa at 589C. A slight decrease in number density was observed in the sample irradiated to 158 dpa at 709CC. The hardness of any of the irradiated samples was almost unchanged from that of the unirradiated sample. It was revealed that the oxide particles existed stable, and the strength of the material was sufficiently maintained even after being neutron irradiated to high dose of 
160 dpa at high temperature up to 700C. A part of this study includes the results of MEXT Innovative Nuclear Research and Development Program Grant Number JPMXD0219214482.
Tsutagi, Koichi; Seki, Masayuki; Tobita, Noriyuki; ; ;
PNC TN8410 91-174, 40 Pages, 1991/02
None
Yano, Yasuhide; Toyama, Takeshi*; Tanno, Takashi; Otsuka, Satoshi; Mitsuhara, Masatoshi*; Nakashima, Hideharu*; Onuma, Masato*; Kaito, Takeji
no journal, ,
no abstracts in English