Nakano, Junichi; Tsukada, Takashi; Tsuji, Hirokazu; Terakado, Shogo; Koya, Toshio; Endo, Shinya
JAERI-Tech 2003-092, 54 Pages, 2004/01
Irradiation assisted stress corrosion cracking (IASCC) is a degradation phenomenon caused by synergy of neutron radiation, aqueous environment and stress on in-core materials, and it is an important issue in accordance with increase of aged light water reactors. Isolating crack initiation stage from crack growth stage is very useful for the evaluation of the IASCC behavior. Hence facility for in-situ observation during slow strain rate test (SSRT) for irradiated material was developed. As performance demonstrations of the facility, tensile test with in-situ observation and SSRT without observation were carried out using unirradiated type 304 stainless steel in 561 K water at 9 MPa. The following were confirmed from the results. (1) Handling, observation and recording of specimen can be operated using manipulators in the hot cell. (2) In-situ observation can be performed in pressurized high temperature water and flat sheet type specimen is suitable for the in-situ observation. (3) Test condition can be kept constantly and data can be obtained automatically for long test period.
Kimura, Hideo; Takahashi, Tomoyuki; ; Matsuzuru, Hideo
JAERI-Research 94-028, 50 Pages, 1994/11
no abstracts in English