伊東 達矢; Xu, S.*; Xu, X.*; 大森 俊洋*; 貝沼 亮介*
Shape Memory and Superelasticity, 9 Pages, 2025/00
The microstructure, crystal structures, cold workability, and martensitic transformation temperatures of several Cu
Mn
Al
(40 
55; 10 
13; at%) alloys were analyzed. For the first time, martensitic transformation was revealed Mn-rich Cu-Mn-Al alloys. The surface relief of the martensite phase reversibly appeared and disappeared during cooling and heating, along with small thermal hysteresis, implying a thermoelastic transformation. The crystal structures of the parent and martensite phases are B2 and 2M(BCT), respectively, with c
Mn
Al
(at%) sample. This alloy demonstrates moderate cold workability and cost-effectiveness, exhibiting potential as an alternative for conventional shape memory alloys in various applications.
星屋 泰二; 田昭 治*; 勝田 博司; 安藤 弘栄
日本金属学会誌, 56(7), p.747 - 756, 1992/00
低圧水素(1.1~78.5kPa)を吸収させたTi-50.5at.%Ni合金について、電気抵抗測定、引張試験、X線回折及び組織観察を行ない、Ti-Ni系合金の変態特性及び変形挙動に及ぼす水素の影響について調べた。電気抵抗測定及び引張試験結果から、この合金のM
温度は水素濃度とともに低下した。これは試料冷却過程のX線回折実験から判明した、水素による母相の安定化現象、すなわちマルテンサイト変態遅滞効果に対応する。すべり変形誘起応力は水素濃度とともに変化した。水素濃度が0.032mol%を越える場合は固溶体硬化現象(hardening)が、0.032mol%以下の場合は固溶体軟化現象(softening)が支配的であった。水素濃度が1.9mol%以上になると水素化物が形成した。これは組織観察において確認されたR相の兄弟晶の再配列や水素吸蔵後の母相格子の格子歪増加と関連する。
星屋 泰二; 高田 文樹; 木崎 實; 田昭 治*; 須藤 健次; 坂倉 敦; 市橋 芳徳
JAERI-M 89-205, 68 Pages, 1989/12
相変態材料に関する照射後物性データは、相変態挙動研究に必要な遠隔操作型温度可変式物性測定装置が開発されていないため殆ど報告されていない。このため形状記憶合金特有の形状特性と密接に関連する照射後変態特性変化を解明する目的で、温度可変式の遠隔操作型電気抵抗測定装置を初めて開発した。更にその装置を用いた形状記憶合金の照射後等時焼鈍実験及び等温焼鈍実験(照射後試験)を実施した。その結果、本装置に用いた単純試料駆動方式による温度制御方法はガンマ線感受性の高い半導体や温度センサーを使用しないため操作性及び信頼性の点からも遠隔操作型物性測定装置に最適であり、他の遠隔操作型装置への応用も可能であることが判明した。遠隔操作型電気抵抗測定装置は照射後の物性測定を行ううえで簡便な実験手段であり、構造敏感(structure sensitive)であるため中性子照射感受性の高い相変態材料の研究に有用である。