Refine your search:     
Report No.
 - 
Search Results: Records 1-7 displayed on this page of 7
  • 1

Presentation/Publication Type

Initialising ...

Refine

Journal/Book Title

Initialising ...

Meeting title

Initialising ...

First Author

Initialising ...

Keyword

Initialising ...

Language

Initialising ...

Publication Year

Initialising ...

Held year of conference

Initialising ...

Save select records

JAEA Reports

Structural investigation of borosilicate glasses by using XAFS measurement in soft X-ray region, 3 (Joint research)

Nagai, Takayuki; Okamoto, Yoshihiro; Yamagishi, Hirona*; Shibata, Daisuke*; Kojima, Kazuo*; Hasegawa, Takehiko*; Sato, Seiichi*; Fukaya, Akane*; Hatakeyama, Kiyoshi*

JAEA-Research 2023-004, 45 Pages, 2023/09

JAEA-Research-2023-004.pdf:6.07MB

The local structure of glass-forming elements and waste elements in borosilicate glasses varies with its chemical composition. In this study, simulated waste glass samples were prepared and the chemical state regarding boron (B), silicon (Si) and waste elements of iron (Fe), cesium (Cs) were estimated by using XAFS measurement in soft X-ray region. To understand the chemical stability of simulated waste glasses, XANES spectra of B K-edge, Fe L$$_{3}$$, L$$_{2}$$-edge, and Cs M$$_{5}$$, M$$_{4}$$-edge were measured on the glass surface exposed to the leachate. As a result, it was found that the glass surface exposed to the leachate was changed and it was difficult to obtain a clear XANES spectrum. From the B K-edge XANES spectra on glass surfaces exposed to the leachate, an increase in three-coordination of B-O (BO$$_{3}$$) and a decrease in four-coordination of B-O (BO$$_{4}$$) were observed compared to the glass surfaces before immersion. The XANES spectra of Fe L$$_{3}$$, L$$_{2}$$-edge, and Cs M$$_{5}$$, M$$_{4}$$-edge show that as the exposure time in the leachate increases, the Cs present on the glass surface dissolves into the leachate. The XANES spectra of Si K-edge were measured on simulated waste glass surfaces before immersion, and it was confirmed that the change in XANES spectra given by Na$$_{2}$$O concentration had a larger effect than the waste component concentration.

JAEA Reports

Structural investigation of borosilicate glasses by using XAFS measurement in soft X-ray region, 2 (Joint research)

Nagai, Takayuki; Okamoto, Yoshihiro; Yamagishi, Hirona*; Kojima, Kazuo*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*

JAEA-Research 2022-008, 37 Pages, 2022/10

JAEA-Research-2022-008.pdf:5.27MB

The local structure of glass-forming elements and waste elements in borosilicate glasses varies with its chemical composition. In this study, borosilicate glass frit and simulated waste glass samples were prepared and the chemical state regarding boron (B), silicon (Si) and waste elements of iron (Fe), cesium (Cs) were estimated by using XAFS measurement in soft X-ray region. Following results were obtained by XAFS measurements of simulated waste glass surfaces after immersion test to investigate the long chemical stability. (1) As the leaching time of glass samples in immersion test passed, the Cs M$$_{5}$$, M$$_{4}$$-edge XANES spectra disappeared and the Fe L$$_{3}$$, L$$_{2}$$-edge spectra changed. (2) A new compound was formed on the sample surface after the immersion test, and these changes in the surface state were confirmed by Raman spectroscopy. However, it became difficult to obtain a clear B K-edge XANES spectrum by forming a compound on glass surfaces. The Si K-edge XANES spectra of borosilicate glass frits with different Na$$_{2}$$O content were measured, and following was confirmed. (1) As the Na$$_{2}$$O concentration increases in borosilicate glass frit, the K-edge peak of Si shifts to the low energy side. (2) The intensity of the Si K-edge peak is maximum when the Na$$_{2}$$O content in glass frits was about 7wt%.

JAEA Reports

Structural investigation of borosilicate glasses by using XAFS measurement in Soft X-ray region (Joint research)

Nagai, Takayuki; Okamoto, Yoshihiro; Yamagishi, Hirona*; Ota, Toshiaki*; Kojima, Kazuo*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*

JAEA-Research 2021-010, 62 Pages, 2022/01

JAEA-Research-2021-010.pdf:6.05MB

The local structure of glass-forming elements and waste elements in borosilicate glasses varies with its chemical composition. In this study, borosilicate glass frit and simulated waste glass samples were prepared and the local structure and chemical state regarding boron(B), oxygen(O), silicon(Si) and waste elements of iron(Fe), cesium(Cs) were estimated by using XAFS measurement in soft X-ray region. Following results were obtained by XAFS measurements of prepared glass frit and simulated waste glass samples: (1) The effect of Na$$_{2}$$O concentration on B-O coordination structure is greater than that of the waste elements concentration. (2) The height of pre-edge by O K-edge spectrum depends on the concentration of first transition elements such as Fe in glass samples. Following results were obtained by XAFS measurements of simulated waste glass samples after immersion test to investigate the long chemical stability. (1) A new compound was formed on the sample surface after the immersion test, and changes in the surface state were confirmed by Raman spectroscopy. (2) Cs on the sample surface after immersion test dissolves into the leaching solution. The Si K-edge XANES spectra of borosilicate glass frits and simulated waste glass samples included lanthanides oxide were measured, and following was confirmed. (1) As the Na$$_{2}$$O concentration increases in borosilicate glass frit, the K-edge peak of Si shifts to the low energy side. (2) The peak height of the K-edge of Si differs depending on the kind of lanthanide.

JAEA Reports

Structural investigation of simulated waste glass samples by using XAFS measurement in soft X-ray region (Joint research)

Nagai, Takayuki; Okamoto, Yoshihiro; Yamagishi, Hirona*; Ota, Toshiaki*; Kojima, Kazuo*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*

JAEA-Research 2020-009, 48 Pages, 2020/09

JAEA-Research-2020-009.pdf:4.53MB

The local structure of glass-forming elements and waste elements in waste glass varies with its chemical composition. In this study, borosilicate glass frit and simulated waste glass samples were prepared and the local structure and chemical state regarding boron (B), oxygen (O), and waste elements of cerium (Ce), cesium (Cs) were estimated by using XAFS measurement in soft X-ray region. Following results were obtained by XAFS measurements of prepared glass frit and simulated waste glass samples: (1) The existence ratio of four coordinate sp$$^{3}$$ structure (BO$$_{4}$$) tends to increase with increasing Na$$_{2}$$O content in glass samples. (2) The height of a pre-edge which appears by K-edge XANES spectrum of O is so high that the Fe content in glass samples. Following results were obtained by XAFS measurements of simulated waste glass samples after immersion test to investigate long chemical stability. (1) The existence ratio of four coordinate sp$$^{3}$$ structure (BO$$_{4}$$) increases by immersion test. (2) Ce which exists in the surface layer is oxidized by immersion test, and much of Cs in surface layer is lost after leach testing. Even if the glass frit form (fiber cartridge or beads) and manufacturing method were changed and a glass sample of the similar chemical composition was prepared, these observed Raman spectra of samples were different.

JAEA Reports

XAFS measurement of simulated waste glass samples (Joint research)

Nagai, Takayuki; Sasage, Kenichi; Okamoto, Yoshihiro; Shiwaku, Hideaki; Yamagishi, Hirona*; Ota, Toshiaki*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*; Takahashi, Tomoe*; et al.

JAEA-Research 2019-003, 94 Pages, 2019/09

JAEA-Research-2019-003.pdf:7.92MB

The local structures of glass-forming elements and waste elements would change by the chemical composition of waste glass including those elements. In this study, simulated waste glass samples were prepared from borosilicate glass frit including phosphorus (P) or vanadium (V), and we investigated local structures of boron, sodium, and waste elements in these P glass and V glass samples by using synchrotron XAFS measurements in soft and hard X ray region.

Oral presentation

XAFS analysis of simulated radioactive waste glasses

Nagai, Takayuki; Okamoto, Yoshihiro; Yamagishi, Hirona*; Ota, Toshiaki*

no journal, , 

no abstracts in English

Oral presentation

Change in B-O coordination structure by chemical composition of borosilicate glass

Nagai, Takayuki; Okamoto, Yoshihiro; Kaneko, Koji; Motokawa, Ryuhei; Haga, Yoshinori; Yamagishi, Hirona*; Yamanaka, Keisuke*; Ota, Toshiaki*

no journal, , 

no abstracts in English