Nagai, Takayuki; Okamoto, Yoshihiro; Yamagishi, Hirona*; Ota, Toshiaki*; Kojima, Kazuo*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*
JAEA-Research 2021-010, 62 Pages, 2022/01
JAEA-Research-2021-010.pdf:6.05MB
The local structure of glass-forming elements and waste elements in borosilicate glasses varies with its chemical composition. In this study, borosilicate glass frit and simulated waste glass samples were prepared and the local structure and chemical state regarding boron(B), oxygen(O), silicon(Si) and waste elements of iron(Fe), cesium(Cs) were estimated by using XAFS measurement in soft X-ray region. Following results were obtained by XAFS measurements of prepared glass frit and simulated waste glass samples: (1) The effect of Na
O concentration on B-O coordination structure is greater than that of the waste elements concentration. (2) The height of pre-edge by O K-edge spectrum depends on the concentration of first transition elements such as Fe in glass samples. Following results were obtained by XAFS measurements of simulated waste glass samples after immersion test to investigate the long chemical stability. (1) A new compound was formed on the sample surface after the immersion test, and changes in the surface state were confirmed by Raman spectroscopy. (2) Cs on the sample surface after immersion test dissolves into the leaching solution. The Si K-edge XANES spectra of borosilicate glass frits and simulated waste glass samples included lanthanides oxide were measured, and following was confirmed. (1) As the NaO concentration increases in borosilicate glass frit, the K-edge peak of Si shifts to the low energy side. (2) The peak height of the K-edge of Si differs depending on the kind of lanthanide.
Nagai, Takayuki; Okamoto, Yoshihiro; Yamagishi, Hirona*; Ota, Toshiaki*; Kojima, Kazuo*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*
JAEA-Research 2020-009, 48 Pages, 2020/09
JAEA-Research-2020-009.pdf:4.53MB
The local structure of glass-forming elements and waste elements in waste glass varies with its chemical composition. In this study, borosilicate glass frit and simulated waste glass samples were prepared and the local structure and chemical state regarding boron (B), oxygen (O), and waste elements of cerium (Ce), cesium (Cs) were estimated by using XAFS measurement in soft X-ray region. Following results were obtained by XAFS measurements of prepared glass frit and simulated waste glass samples: (1) The existence ratio of four coordinate sp
structure (BO
) tends to increase with increasing NaO content in glass samples. (2) The height of a pre-edge which appears by K-edge XANES spectrum of O is so high that the Fe content in glass samples. Following results were obtained by XAFS measurements of simulated waste glass samples after immersion test to investigate long chemical stability. (1) The existence ratio of four coordinate sp structure (BO) increases by immersion test. (2) Ce which exists in the surface layer is oxidized by immersion test, and much of Cs in surface layer is lost after leach testing. Even if the glass frit form (fiber cartridge or beads) and manufacturing method were changed and a glass sample of the similar chemical composition was prepared, these observed Raman spectra of samples were different.
Nagai, Takayuki; Sasage, Kenichi; Okamoto, Yoshihiro; Shiwaku, Hideaki; Yamagishi, Hirona*; Ota, Toshiaki*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*; Takahashi, Tomoe*; et al.
JAEA-Research 2019-003, 94 Pages, 2019/09
JAEA-Research-2019-003.pdf:7.92MB
The local structures of glass-forming elements and waste elements would change by the chemical composition of waste glass including those elements. In this study, simulated waste glass samples were prepared from borosilicate glass frit including phosphorus (P) or vanadium (V), and we investigated local structures of boron, sodium, and waste elements in these P glass and V glass samples by using synchrotron XAFS measurements in soft and hard X ray region.
Nagai, Takayuki; Okamoto, Yoshihiro; Shiwaku, Hideaki; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*; Hirono, Kazuya*; Homma, Masanobu*; Kobayashi, Hiromi*; Takahashi, Tomoe*; et al.
JAEA-Research 2018-007, 87 Pages, 2018/11
JAEA-Research-2018-007.pdf:61.21MB
To select the chemical composition of a glass frit which can increase the waste content, the simulated waste glass samples prepared from a borosilicate glass frit including vanadium (V) were investigated by using Laser Ablation (LA) ICP-AES analysis, Raman spectrometry, and synchrotron XAFS measurement in this study on foundation business of the Agency for Natural Resources and Energy.
Yamamoto, Ken; Kobori, Tetsuo; Kanegae, Naomichi; Ozawa, Kenji; Komiya, Kazuyoshi; Tsubota, Toshihide; Nakashima, Fumiaki; Noda, Kimio; Suzuki, Takeo; Yoshino, Kenichi; et al.
PNC TN2450 93-001, 190 Pages, 1993/03
no abstracts in English
Kitahara, Yasuko*; Inose, Akira*; Makiishi, Noriko*; Nagoshi, Masayasu*
no journal, ,
no abstracts in English