Miyagi, Masanori*; Hongze, W.*; Yoshida, Ryohei*; Kawahito, Yosuke*; Kawakami, Hiroshi*; Shobu, Takahisa
Scientific Reports (Internet), 8(1), p.12944_1 - 12944_10, 2018/08
Times Cited Count：42 Percentile：81.46(Multidisciplinary Sciences)The behavior inside the metal during laser welding is very important because it greatly affects the material strength, defect generation, and so on. In this study, weld pool dynamics in laser welding of various series of aluminum alloys were investigated by the 
synchrotron radiation X-ray phase contrast imaging system. The experimental results showed that metal irradiated by laser was evaporated immediately, which generated the keyhole. Then metal surrounding the keyhole was melted gradually with the heat from keyhole. The growth rate of keyhole depth had a positive linear correlation with the total content of low boiling temperature elements (TCE), so did the keyhole depth and diameter at the stable stage. Then, by repeating the experiment, we succeeded in quantifying the effect of alloying elements on the dynamics of the weld pool in laser welding of aluminum alloys.
Saito, Shigeru; Kikuchi, Kenji*; Hamaguchi, Dai; Tezuka, Masao*; Miyagi, Masanori*; Kokawa, Hiroyuki*; Watanabe, Seiichi*
Journal of Nuclear Materials, 431(1-3), p.91 - 96, 2012/12
Times Cited Count：16 Percentile：75.52(Materials Science, Multidisciplinary)To evaluate lifetime of structural materials for ADS, corrosion tests in LBE have been done at JAEA. The corrosion test was performed by using JAEA lead-bismuth flowing loop (JLBL-1). Experimental condition was as follows; The temperature of high and low temperature parts of the loop were 450
C and 350C, respectively. Flowing velocity at the test specimens was about 1m/s. Plate type SS316L-BM and SS316L-GBEM were used as a specimens. After the 3,000 hours operation, the test specimens were cut and macroscopic observation was carried out. The result showed that both materials were intensively eroded. Corrosion depth and LBE penetration through grain boundaries of GBEM were smaller than these of 316SS-BM.
Yamashita, Shinichiro; Yano, Yasuhide; Endo, Masaki*; Sakaguchi, Norihito*; Watanabe, Seiichi*; Miyagi, Masanori*; Sato, Shinya*; Sato, Yutaka*; Kokawa, Hiroyuki*; Kawai, Masayoshi*
no journal, ,
no abstracts in English
Yano, Yasuhide; Yamashita, Shinichiro; Endo, Masaki*; Sakaguchi, Norihito*; Watanabe, Seiichi*; Miyagi, Masanori*; Oyamada, Tetsuya*; Sato, Shinya*; Sato, Yutaka*; Kokawa, Hiroyuki*; et al.
no journal, ,
no abstracts in English
Saito, Shigeru; Kikuchi, Kenji; Hamaguchi, Dai; Tezuka, Masao; Miyagi, Masanori*; Kokawa, Hiroyuki*
no journal, ,
no abstracts in English