Kuroda, Masatoshi*; Kamaya, Masayuki*; Yamada, Teruaki*; Akita, Koichi
Nihon Kikai Gakkai Rombunshu (Internet), 83(852), p.17-00072_1 - 17-00072_7, 2017/07
In order to assess the fatigue damage of austenitic stainless steels by electron backscatter diffraction (EBSD) method more simply and easily, it should be more preferable to use a commercially available general-purpose EBSD analysis software rather than to employ an in-house developed EBSD analysis programme. In the present study, EBSD measurement was performed for Type 316 austenitic stainless steels subjected to cyclic loading, and the applicability of the EBSD parameter relevant to the pattern quality, which could be obtained by the commercial software, to the fatigue damage assessment was discussed by comparing the other EBSD parameter of the averaged local misorientation (Mave), which could be calculated by the in-house developed programme. As a result, the EBSD parameter relevant to the pattern quality, which signified the full width at half maximum (FWHM) of the histogram distribution of the image quality (IQ), was saturated at the beginning stage of the fatigue cycles, while Mave was increased monotonically with the cycles. This suggested that the FWHM of IQ could be useful to detect the initial stage of the fatigue damage, while Mave was suitable for the quantitative evaluation of the fatigue damage. XRD measurement was also carried out for the same samples employed in the EBSD measurement, and the XRD data was compared with the EBSD data to discuss the crystallographic mechanism of the change in the FWHM of IQ. As a result, it was found that the FWHM of the (111) XRD peak correlated well with the FWHM of IQ. Because the (111) plane in fcc metal such as austenitic stainless steel was most preferable for slip system, this implied that the change in the distribution of the pattern quality generated by the fatigue loading could be due to the slip deformation.
Yamada, Teruaki*; Matsushima, Yuki*; Kuroda, Masatoshi*; Sumita, Junya; Shibata, Taiju; Fujita, Ichiro*; Sawa, Kazuhiro
Nuclear Engineering and Design, 271, p.323 - 326, 2014/05
Times Cited Count：13 Percentile：70.2(Nuclear Science & Technology)In order to investigate the effects of the experimental methodology and the notch angle on the fracture toughness of the fine-grained isotropic nuclear graphites IG-110 and IG-430, the three-point-bending test, which has been recently proposed as the methodology to evaluate the fracture toughness of graphite for high temperature gas-cooled reactors (HTGRs), was performed using two types of the specimens with different notch angles. The results obtained in this study could be summarized as follows: (1) The values of the fracture toughness of IG-110 and IG-430 measured in this study were 0.890 MPa m
and 1.031 MPa m, respectively. It was also found that the value of the fracture toughness of IG-110 was nearly equal to or smaller than the values obtained by the other method reported previously. (2) The values of the fracture toughness of the fine-grained isotropic graphites were not affected between the notch angles introduced by the incisive razor blade. (3) The ratio of the tensile strengths of IG-110 and IG-430 was estimated from Griffith Theory using the experimental data obtained in this study. The estimated strength ratio was in good agreement with the strength ratio obtained from the supplier's data.
Yamada, Teruaki*; Matsushima, Yuki*; Kuroda, Masatoshi*; Sumita, Junya; Shibata, Taiju; Fujita, Ichiro*; Sawa, Kazuhiro
Proceedings of 6th International Topical Meeting on High Temperature Reactor Technology (HTR 2012) (USB Flash Drive), 6 Pages, 2012/10
In order to investigate the effects of the experimental methodology and the notch angle on the fracture toughness of the fine-grained isotropic nuclear graphites IG-110 and IG-430, the three-point-bending test, which has been recently proposed as the methodology to evaluate the fracture toughness of graphite for high temperature gas-cooled reactors (HTGRs), was performed using two types of the specimens with different notch angles. The results obtained in this study could be summarized as follows: (1) The values of the fracture toughness of IG-110 and IG-430 measured in this study were 0.890 (MPam) and 1.031 (MPam), respectively. It was also found that the value of the fracture toughness of IG-110 was nearly equal to or smaller than the values obtained by the other method reported previously. (2) The values of the fracture toughness of the fine-grained isotropic graphites were not affected between the notch angles introduced by the incisive razor blade. (3) The ratio of the tensile strengths of IG-110 and IG-430 was estimated from Griffith Theory using the experimental data obtained in this study. The estimated strength ratio was in good agreement with the strength ratio obtained from the supplier's data.
Matsushima, Yuki*; Yamada, Teruaki*; Kuroda, Masatoshi*; Sumita, Junya; Shibata, Taiju; Sawa, Kazuhiro
no journal, ,
In order to investigate the effect of notch-tip geometry on the fracture toughness of fine-grained isotropic graphite ETU-10, three-point-bending fracture toughness tests have been performed by using two types of single-edge notched beam specimens with different notch angles of approximately 15
and 30. The values of the fracture toughness were calculated based on linear elastic fracture mechanics by using the maximum force which could be obtained by the load-displacement curve. As a result, the values of the fracture toughness of the specimens with the notch angles of approximately 15 and 30 were 0.933 MPa mand 0.926 MPa m, respectively. This suggested that the values of the fracture toughness were not affected between the notch angles. Further work has been ongoing to discuss the effect of the notch-tip geometry such as angle and root radius of notch in terms of finite element analysis.
Kuroda, Masatoshi*; Kamaya, Masayuki*; Akita, Koichi; Yamada, Teruaki*; Shimasaki, Tomonori*; Tanigawa, Ryohei*
no journal, ,
no abstracts in English