Importance of fracture criterion and crack tip material characterization in probabilistic fracture mechanics analysis of an RPV under a pressurized thermal shock

Shibata, Katsuyuki; Onizawa, Kunio ; Li, Y.* ; Kato, Daisuke*

The paper describes the procedure to evaluate the ductile crack extension, where an increase in fracture resistance by a ductile crack extension is considered. Two standard -resistance curves are prepared for applying the elasto-plastic fracture criterion. Case studies concerning the effect of elasto-plastic fracture criterion were carried out using a severe PTS transient. The introduction of the elasto-plastic fracture criterion significantly contributes to remove the over-conservatism in applying the linear elastic fracture criterion. It was also found that the algorithm of the re-evaluation of crack tip characterization also has a significant effect on the failure probability.