Penetration behavior of solution containing radioactive nuclides into floor and wall materials

Usuki, Toshiyuki ; Sato, Isamu; Suto, Mitsuo; Maeda, Koji  ; Osaka, Masahiko  ; Koyama, Shinichi  ; Tokoro, Daishiro*; Sekioka, Ken*; Ishigamori, Toshio*

The penetration tests with solution containing radioactive nuclides were experimented to understand basic data for floor and wall materials of Fukushima Daiichi reactor buildings. The solution prepared from irradiated fuels was used as solution containing radioactive nuclides. The solution was applied to surface of epoxy paint, dried concrete and mortar used as specimens. Dose-rate profiles of direction of depth were given by radiation measurement and grinding of the specimens. The penetrations of radioactive nuclides for epoxy paint specimens were not clearly observed and the penetration depths would be within 0.4 mm. The penetrations of radioactive nuclides for dried concrete specimens proceeded. The penetration rates were substantially decreased when 16 days have elapsed from start. The dose rates of penetrated dried concrete specimens were reduced to background by grinding-2.0 mm. -ray spectrometry measurement showed that penetration behavior of near surface concrete are different among nuclides and the penetration behavior of radioactive nuclides into dried concrete and mortar materials through solution is similar to migration behavior of ions into those water-saturated materials.