Structural investigation of borosilicate glasses by using XAFS measurement in Soft X-ray region (Joint research)

Nagai, Takayuki  ; Okamoto, Yoshihiro  ; Yamagishi, Hirona*; Ota, Toshiaki*; Kojima, Kazuo*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*

The local structure of glass-forming elements and waste elements in borosilicate glasses varies with its chemical composition. In this study, borosilicate glass frit and simulated waste glass samples were prepared and the local structure and chemical state regarding boron(B), oxygen(O), silicon(Si) and waste elements of iron(Fe), cesium(Cs) were estimated by using XAFS measurement in soft X-ray region. Following results were obtained by XAFS measurements of prepared glass frit and simulated waste glass samples: (1) The effect of Na$$_{2}$$O concentration on B-O coordination structure is greater than that of the waste elements concentration. (2) The height of pre-edge by O K-edge spectrum depends on the concentration of first transition elements such as Fe in glass samples. Following results were obtained by XAFS measurements of simulated waste glass samples after immersion test to investigate the long chemical stability. (1) A new compound was formed on the sample surface after the immersion test, and changes in the surface state were confirmed by Raman spectroscopy. (2) Cs on the sample surface after immersion test dissolves into the leaching solution. The Si K-edge XANES spectra of borosilicate glass frits and simulated waste glass samples included lanthanides oxide were measured, and following was confirmed. (1) As the Na$$_{2}$$O concentration increases in borosilicate glass frit, the K-edge peak of Si shifts to the low energy side. (2) The peak height of the K-edge of Si differs depending on the kind of lanthanide.

Acecsses

:

- Accesses

InCites™

:

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.