Iwata, Keiko; Hata, Kuniki; Tobita, Toru; Hirota, Takatoshi*; Takamizawa, Hisashi; Chimi, Yasuhiro; Nishiyama, Yutaka
Proceedings of ASME 2021 Pressure Vessels and Piping Conference (PVP 2021) (Internet), 7 Pages, 2021/07
Tobita, Toru; Nishiyama, Yutaka; Onizawa, Kunio
JAEA-Data/Code 2018-013, 60 Pages, 2018/11
Mechanical properties of materials including fracture toughness are extremely important for evaluating the structural integrity of reactor pressure vessels (RPVs). In this report, the published data of mechanical properties of nuclear RPVs steels, including neutron irradiated materials, acquired by the Japan Atomic Energy Agency (JAEA), specifically tensile test data, Charpy impact test data, drop-weight test data, and fracture toughness test data, are summarized. There are five types of RPVs steels with different toughness levels equivalent to JIS SQV2A (ASTM A533B Class 1) containing impurities in the range corresponding to the early plant to the latest plant. In addition to the base material of RPVs, the mechanical property data of the two types of stainless overlay cladding materials used as the lining of the RPV are summarized as well. These mechanical property data are organized graphically for each material and listed in tabular form to facilitate easy utilization of data.
Tobita, Toru; Nishiyama, Yutaka; Otsu, Takuyo; Udagawa, Makoto; Katsuyama, Jinya; Onizawa, Kunio
Journal of Pressure Vessel Technology, 137(5), p.051405_1 - 051405_8, 2015/10
Times Cited Count:14 Percentile:54.16(Engineering, Mechanical)We conducted a series of fracture toughness tests based on the Master curve method for several specimen size and shapes, such as 0.16T-CT, pre-cracked Charpy type, 0.4T-CT and 1T-CT specimens, in commercially manufactured 5 kinds of A533B class1 steels with different impurity contents and fracture toughness levels. The reference temperature () values determined from the 0.16T-CT specimens were overall in good agreement with those determined from the 1T-CT specimens. The scatter of the 1T-equivalent fracture toughness values obtained from the 0.16T-CT specimens was equivalent to that obtained from the other larger specimens. The higher loading rate gave rise to a slightly higher , and this dependency was almost the same for the larger specimens. We suggested an optimum test temperature on the basis of the Charpy transition temperature for determining using the 0.16T-CT specimens.
Tachibana, Yukio; Nakagawa, Shigeaki; Iyoku, Tatsuo
Nuclear Engineering and Design, 233(1-3), p.103 - 112, 2004/10
Times Cited Count:1 Percentile:9.98(Nuclear Science & Technology)no abstracts in English
Tachibana, Yukio; Nakagawa, Shigeaki; Iyoku, Tatsuo
Elevated Temperature Design and Analysis, Nonlinear Analysis, and Plastic Components, 2004 (PVP-Vol.472), p.39 - 44, 2004/07
The reactor pressure vessel (RPV) of the HTTR is 5.5m in inside diameter, 13.2m in inside height, and 122mm and 160mm in wall thickness of the body and the top head dome, respectively. Because the reactor inlet temperature of the HTTR is higher than that of LWRs, 2 1/4Cr-1Mo steel is chosen for the RPV material. Fluence of the RPV is estimated to be less than 110n/cm(E1 MeV), and so irradiation embrittlement is presumed to be negligible, but temper embrittlement is not. For the purpose of reducing embrittlement, content of some elements is limited on 2 1/4 Cr-1 Mo steel for the RPV using embrittlement parameters, J-factor and X-bar. In this paper design, fabrication procedure, and in-service inspection technique of the RPV for the HTTR are described.
*; Tachibana, Yukio; Kunitomi, Kazuhiko;
JAERI-Tech 96-034, 120 Pages, 1996/08
no abstracts in English
Tsukada, Takashi; Suzuki, Masahide; Kawasaki, Satoru
Proceedings of Three Mile Island Reactor Pressure Vessel Investigation Project Open Forum, p.151 - 163, 1994/00
no abstracts in English