佐藤 雄二*; 塚本 雅裕*; 菖蒲 敬久; 舟田 義則*; 山下 順広*; 原 崇裕*; 仙石 正則*; 左近 祐*; 大久保 友政*; 吉田 実*; et al.
Applied Surface Science, 480, p.861 - 867, 2019/06
被引用回数:32 パーセンタイル:83.50(Chemistry, Physical)A blue direct diode laser metal deposition system, which uses multiple lasers, was developed to realize a high-quality coating layer with a dense, fine structure and high purity. To clarify the formation mechanism of the pure copper layer, the formation process using a blue direct diode laser system was observed using in situ X-ray observations. The stainless steel 304 substrate melts, generating bubbles in the molten pool at a laser power density of 7.2 10 W/cm and a scanning speed of 3.0 mm/s. At a laser scanning speed of 9.0 mm/s, the bubbles disappear because only a slightly molten pool is formed on the surface of the substrate. The bubble amount and penetration depth depend on the laser input energy with a blue direct diode laser. By controlling the amount of input energy, a copper coating is produced minutely without a weld penetration.
佐藤 雄二*; 塚本 雅裕*; 菖蒲 敬久; 山下 順広*; 山縣 秀人*; 西 貴哉*; 東野 律子*; 大久保 友政*; 中野 人志*; 阿部 信行*
Applied Physics A, 124(4), p.288_1 - 288_6, 2018/04
被引用回数:18 パーセンタイル:64.77(Materials Science, Multidisciplinary)レーザーコーティングによる高品質な金属膜生成をめざし、本研究ではシンクロトロン放射光実験により、レーザー照射により溶融したチタンの動態を調べた。濡れ性の指標として、レーザ照射中を30keVのシンクロトロンX線により、Ti64ベースプレートとTi球との接触角を測定した。その結果、ベースプレートの温度が上昇すると接触角は低下し、ベースプレートの温度が500Cのときに接触角度は28度まで減少することを確認した。そして予熱をした状態でレーザーコーティングを行うとスパッタリングが少なく、表面粗さも少ない高品質な金属膜の生成に成功したが、この要因として濡れ性の改善が大きく関与していることを明らかにした。