鈴木 賢治*; 菖蒲 敬久; 和田 国彦*; 松原 秀彰*; 川村 昌志*
材料, 57(7), p.674 - 680, 2008/07
CoNiCrAlY was pressureless plasma-sprayed on a substrate of nickel-base superalloy as a bond coating. Under the substrate rotation, zirconia with 4mol yttria was coated as the top coating by the electron beam-physical vapor deposition (EB-PVD). The rotation speed of the substrate was 5, 10 and 20rpm. The top coating was made by the columnar structure which consisted of the core part and the peripheral part. The top of the core part had a pyramidal shape made by piling up the zirconia (111) planes. The peripheral part showed feather-like structure, which was made by growth of the zirconia 
100
and (111) directions. By the increase in the rotation speed, the column becomes thick and the inter-columnar space becomes large. The substrate rotation is useful for the reduction of the residual stresses in the EB-PVD thermal barrier coating.
鈴木 賢治*; 和田 国彦*; 松原 秀彰*; 菖蒲 敬久; 川村 昌志*; 田中 啓介*
材料, 56(7), p.588 - 593, 2007/07
Niベースの超合金であるIN738LCは基質材料として使われ、CoNiCrAlYはその上にボンドコートとしてプラズマスプレーにより押し固められている。その上にZrがEV-PVD法によりトップコーティングされている。本試験では基盤回転数の異なる試料に関して、組織観察及び残留応力測定を行った。SEM観察の結果から、Zrコーティングは(111)方向に成長した柱状組織を有していることがわかった。また表面の残留応力は、基盤回転数が減少するに従い圧縮の残留応力が大きくなることがわかった。
鈴木 賢治*; 川村 昌志*; 菖蒲 敬久; 田中 啓介*; 秋庭 義明*
材料, 55(7), p.634 - 640, 2006/07
プラズマ溶射された遮熱コーティング(TBC)の残留応力及び機械的挙動は、高温機器の性能にかかわる重要な問題である。本研究では、曲面上にプラズマ溶射されたTBCを高温酸化処理しその際に発生するき裂形態を検討した。その結果、局率半径が小さくなるに従い測定された半径応力は大きくなることを見いだした。また半径応力の最大値とはく離き裂密度との比較から、はく離き裂の発生は局率半径の減少により促進される結果を得た。
西尾 敏; 阿部 哲也; 川村 昌志*; 山崎 誠一郎*
JAERI-Tech 94-006, 18 Pages, 1994/08
核融合の環境下で高い信頼性を有する配管の絶縁継手として、中央部をセラミックス、両端部を溶接可能な金属、中間領域には両者の成分を緩やかに傾斜させたパイプ要素を開発してきた。積層粉体の焼結成形で得られる機能傾斜材の最大の技術課題は焼結温度から室温に至る過程で発生する残留熱応力の緩和対策である。詳細な応力解析と幾つかの試作を通して適切な焼結条件を設定することが可能となり、実機に適用し得る機能傾斜型電気絶縁継手の試作に成功した。更に大型FGMの製造技術に不可欠な焼結バランスの制御についても基本技術が確立され、大型配管への適用見通しが得られた。