XAFS measurement of simulated waste glass samples (Borosilicate glass including vanadium)

Nagai, Takayuki; Kobayashi, Hidekazu; Sasage, Kenichi; Ayame, Yasuo; Okamoto, Yoshihiro; Shiwaku, Hideaki; Matsuura, Haruaki*; Uchiyama, Takafumi*; Okada, Yukiko*; Nezu, Atsushi*; et al.

JAEA-Research 2016-015, 52 Pages, 2016/11

JAEA-Research-2016-015.pdf:37.48MB

The local structure of waste elements in simulated waste glasses including V was estimated by using synchrotron XAFS measurement in this study. The results are as follows. (1) V has a high possibility which exists in the glass phase in the case of frit, and V can regard both samples as stable 4 coordination structure. (2) Zn, Ce, Nd, Zr, and Mo exist in the glass phase, and the difference is admitted by the percentage of Ce(III) and Ce(IV) by the composition. (3) Ru is separated from the glass phase as RuO crystalline, both of metal and oxide exist in Rh, and Pd is separated out as metal. (4) It was confirmed that the regularity of the local structure of Zr and Mo in the molten glasses retreats as a result of the XAFS measurement at high temperature. (5) The XAFS measurement of molten glasses were performed at 1200C, so it would be possible to acquire excellent data by improving the shapes of the sample cell.