Hydrogenation of a TiFe-based alloy at high pressures and temperatures

高温高圧下でのTiFe基合金の水素化

遠藤 成輝*; 斉田 愛子*; 中村 優美子*; 齋藤 寛之; 町田 晃彦

Endo, Naruki*; Saita, Itoko*; Nakamura, Yumiko*; Saito, Hiroyuki; Machida, Akihiko

We investigated the hydrogenation of a ternary TiFe$$_{0.8}$$Mn$$_{0.2}$$ alloy under high pressure (up to 6.5 GPa) and at high temperature (up to 600 $$^{circ}$$C) by in situ synchrotron radiation X-ray diffraction measurements. A chemical order-disorder phase transition and the formation of body-centered cubic (BCC) hydride were observed. The phase-transition temperature was 400 $$^{circ}$$C, which is 200 $$^{circ}$$C lower than that of a binary TiFe alloy. A disproportionation reaction, which was observed for the binary TiFe alloy, did not occur at this temperature. The BCC hydride existed stably, and new hydrides were not formed after the BCC hydride became a single phase. Since the unit cell volume of the BCC hydride was almost equal to that of the hydride, TiFe$$_{0.8}$$Mn$$_{0.2}$$H$$_{1.8}$$, under the same pressure-temperature conditions, the hydrogen content of the former was roughly estimated as the same as that of the latter (hydrogen to metal atom ratio = 0.9).

Access

:

- Accesses

InCites™

:

パーセンタイル:70.76

分野:Chemistry, Physical

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.