Electrochemical reaction mechanisms under various charge-discharge operating conditions for Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$ in a lithium-ion battery

リチウムイオン電池正極材料Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$の充放電過程における電気化学反応のメカニズムの研究

小西 宏明*; 平野 辰巳*; 高松 大郊*; 軍司 章*; Feng, X.*; 古月 翔*; 奥村 壮文*; 寺田 尚平*; 田村 和久   

Konishi, Hiroaki*; Hirano, Tatsumi*; Takamatsu, Daiko*; Gunji, Akira*; Feng, X.*; Furutsuki, Sho*; Okumura, Takafumi*; Terada, Shohei*; Tamura, Kazuhisa

Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$正極の充電過程において、各SOCでの電極電位は、放電過程より高い。この機構を明らかにするために、様々なSOCにおいて電気化学測定、XRD, XAFS測定を行った。その結果、Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$の格子状数や遷移金属の酸化状態が異なっていることが分かった。また、Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$中に、LiNi$$_{0.33}$$Mn$$_{0.33}$$Co$$_{0.33}$$O$$_{2}$$やLi$$_{2}$$MnO$$_{3}$$に類似した構造が存在することも明らかになった。

The potential in each state of charge (SOC) during charging of Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$ is higher than that during discharging. To clarify the effect of chargedischarge operating conditions on the electrochemical reaction, Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$ was charged and discharged under various charge-discharge operating ranges, and OCP, crystal structure, and oxidation states of the ransition metals were evaluated by electrochemical measurement, XRD, and XAFS. These results indicate that OCP, lattice parameters, and oxidation states of the transition metals of Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$ in each SOC are not constant. The XRD results indicate that two phases, namely, LiNi$$_{0.33}$$Mn$$_{0.33}$$Co$$_{0.33}$$O$$_{2}$$-like and Li$$_{2}$$MnO$$_{3}$$-like, exist in Li$$_{1.2}$$Ni$$_{0.13}$$Mn$$_{0.54}$$Co$$_{0.13}$$O$$_{2}$$.