Rediscovery of Hall-Petch strengthening in bulk ultrafine grained pure Mg at cryogenic temperature; A Combined ${it in situ}$ neutron diffraction and electron microscopy study

Zheng, R.*; Gong, W.   ; Du, J.-P.*; Gao, S.*; Liu, M.*; Li, G.*; 川崎 卓郎   ; Harjo, S.   ; Ma, C.*; 尾方 成信*; 辻 伸泰*

Zheng, R.*; Gong, W.; Du, J.-P.*; Gao, S.*; Liu, M.*; Li, G.*; Kawasaki, Takuro; Harjo, S.; Ma, C.*; Ogata, Shigenobu*; Tsuji, Nobuhiro*

Grain refinement can lead to the strengthening of metallic materials according to the Hall-Petch relationship. However, our recent results suggested that grain boundary sliding is the dominant deformation mode in bulk ultrafine grained (UFG) pure Mg at room temperature, leading to softening. Here, for the first time, we report that the Hall-Petch strengthening can be regained in bulk UFG pure Mg at cryogenic temperature. At 77K, the UFG pure Mg with a mean grain size of 0.6 $$mu$$m exhibited ultrahigh tensile yield strength and ultimate tensile strength of 309 MPa and 380 MPa, respectively. Combined ${it in situ}$ neutron diffraction and electron microscopy investigation indicated that residual dislocation structures and deformation twins hardly formed in the UFG specimen during tensile test at 298K. In contrast, fast accumulation of lattice defects and remarkable reorientation were evident at 77K, suggesting that the grain-boundary-mediated process was suppressed and the plastic deformation was dominated by dislocation slip and deformation twinning. In addition, all the pure Mg specimens exhibited pronounced strain hardening at 77 K, which was mainly attributed to the suppressed grain boundary sliding and dynamic recovery. The mean dislocation density and relative fractions of dislocations with various Burgers vectors of the UFG specimen deformed at 77K were determined quantitatively from neutron diffraction data.

Access

:

- Accesses

InCites™

:

パーセンタイル:94.59

分野:Materials Science, Multidisciplinary

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.